Debinding Defect Formation in Photopolymer-Derived Ceramic and Metal Green Bodies
Segurola, Juan
2026-08-21 · Informe · Versión 1.2
Los títulos y las descripciones bibliográficas se conservan en el idioma del registro original. Los enlaces a los PDF indican los idiomas disponibles.
Three verified topical studies address rapid debinding of Si3N4 green bodies, cure-depth selection for Al2O3 VPP and pyrolysis-kinetics prediction for ceramic VPP binders. This note maps that evidence to a qualification architecture that retains failed parts and inspects defects before sintering. ISO 11358-1:2022 is identified for general thermogravimetric principles, but the actual formulation, atmosphere, heating rate, gas flow, crucible and sample mass remain part of the result. Generic photopolymer reviews are removed from the topic-specific evidence set. RP-02 defines the shared qualification method.